Terblend N NM-19 Properties
Mechanical Properties
Value & Unit
Test Condition
Test Method
Elongation at Break, MD
> 50 %
ISO 527-3
Tensile Modulus
2000 MPa
ISO 527
Tensile Strain
3.5 %
at Yield, 23°C
ISO 527-2
Flexural Strength
62 MPa
ISO 178
Flexural Modulus
1800 MPa
ISO 527
Impact Strength, Notched Charpy
65 kJ/m²
23°C
ISO 179
Hardness, Ball Indentation
86 MPa
ISO 2039-1
Impact Strength, Notched Charpy
15 kJ/m²
-30°C
ISO 179
Hardness, Rockwell
103 R Scale
ISO 2039-2
Tensile Strength, Yield
43 MPa
At 23°C
ISO 527-2
Thermal Properties
Value & Unit
Test Condition
Test Method
Heat Deflection Temperature (HDT), Annealed
85 °C
At 66 psi (0.45 Mpa)
ISO 75-2/B
CTE, Linear
100×10-6 /°C
ISO 11359
Vicat Softening Temperature
160 °C
VST/A/50 (50°C/h, 10N)
ASTM D1525
Vicat Softening Temperature
102 °C
VST/B/50 (50°C/h, 50N)
ISO 306
Heat Deflection Temperature (HDT), Annealed
65 °C
At 264 psi (1.80 Mpa)
ISO 75-2/A
Physical Properties
Value & Unit
Test Condition
Test Method
Melt Volume-Flow Rate (MVR)
30 cm³/10 min
240°C/10 kg
ISO 1133
Moisture Absorption at Equilibrium
1.2 %
50 % R.H
ISO 62
Density
1070 kg/m³
ISO 1183
Electrical Properties
Value & Unit
Test Condition
Test Method
Dissipation Factor
150
1 MHz
IEC 60250
Volume Resistivity
> 1.000E+013 ohm-m
IEC 60093
Relative Permittivity
2.9
1 MHz
IEC 60250
Surface Resistance
1E14 ohm
IEC 60093
Terblend® N NM-19 Processing Guidelines
Injection Molding Properties
Value & Unit
Test Condition
Test Method
Processing (Melt) Temp
240 - 270 °C
Linear Mold shrinkage
0.8 %
Mold Temperature
40 - 80 °C
Screw Length
18 - 23 D
Drying Temperature
80 - 90 °C
Length of Feed Section
0.5 - 0.55 l
Drying Time
4 hr
Length of Compression Section
0.25 - 0.3 l
Suggested Max Moisture
0.1 %
Length of Metering Section
0.2 l
Flight Depth in Feed Section
0.8 - 1.0 D
Flight Depth Ratio
2 - 3
Compression Ratio
2 - 2.5